Abstract：[Background] The domestic sludge contains a large number of nutrients such as nitrogen, phosphorus and potassium, but accumulates a large number of pathogens and organic pollutants such as parasites (eggs).The light particles can be prepared for flower growth by using sludge and adding inorganic powders including clay, quartz sand tailings, diatomaceous earth, and so on. This effectively reuses domestic sludge and avoids environmental pollution from domestic sludge.[Methods] Each raw material was ground using an agate mortar before test to maintain the particle size of the raw material between 200 and 600 mesh. The particle size distribution of each raw material was measured using a Bettersize2000 laser particle size distribution analyzer. The compressive strength of lightweight particles was measured using an ATH-5000 spring tension tester. The microscopic morphology of light particles was analyzed using an EVO-18 scanning electron microscope. The product crystal analysis was carried out by XD-3 X-ray powder diffractometer.[Results] The compressive strength of the light particles decreased from 7.47 to 2.33 MPa, the bulk density decreased from 1.63 to 1.11 g/cm3, and the water absorption rate increased from 33.33 to 63.67%, when the sludge content increased gradually from 0 to 100%. The compressive strength of the light particles increased to 7.35 MPa then began to decline, the bulk density of the light particles increased from 0.91 to 1.20 g/cm3, thus, the water absorption rate gradually decreased from 61.33% to 40.33%, when the contents of clay increased from 0 to 100%. Quartz sand tailings were to increase the content of the SiO2 of the product, and improved compressive strength of the products. The products possessed strong adsorption with water absorption rate of 50%, by the porous structure of diatomaceous earth and the amount of organic matter evaporated in the sludge. The optimal addition amount of each inorganic powder reagent was determined using single-variable control method as domestic sludge 50%, clay 30%, quartz sand tailings 10%, kaolin 5%, diatomaceous earth 2%, Al2(SO4)3 3%, firing temperature 930℃, and holding time 50 min, the compressive strength of the light particles prepared under the optimal conditions was 4.0 MPa, the water absorption rate was 50%, and the nutrient mass fraction N 37.1 mg/g, P 12.5 mg/g, K 4.4 mg/g.[Conclusions] The utilization rate of the domestic sludge is up to 50%, the compressive strength of the light particles is above 7.0 MPa, and the water absorption rate is 50%. The performance of the product particles is superior to the domestic and foreign equivalent products, and meets the vegetation growth requirements of flowers and the like, accorded with national standards GB/T 17431-1998. The conditions provide a simple and easy way to utilize sludge efficiently, and showing certain economic, environmental and social benefits.
张雪梅1, 陈涛1, 付红伦2, 汪徐春1, 况培培1, 刘敏1. 采用生活污泥制备用于花卉生长的轻质颗粒的试验[J]. 中国水土保持科学, 2018, 16(5): 136-144.
ZHANG Xuemei, CHEN Tao, FU Honglun, WANG Xuchun, KUANG Peipei, LIU Min. Experimental preparation of light particles for flower growth using living sludge. SSWC, 2018, 16(5): 136-144.
杨勇.对城市污水厂污泥的处理处置及综合利用分析[J].技术论坛, 2016, (42):231. YANG Yong. Treatment and comprehensive utilization of sludge in municipal wastewater treatment plant[J]. Technology Forum, 2016,(42):231.
[2]
陈亮.城市污水处理厂污泥处置方法分析[J].能源环境, 2014, 131. CHEN Liang.Analysis of sludge disposal methods in urban sewage treatment plants[J]. Energy Environment, 2014, 131.
[3]
姜珊珊,王佳琪.我国污泥处理的现状及相关技术比较[J].科学之友, 2011, 3:158. JIANG Shangshang, WANG Jiaqi. Our country sludge treatment present situation and correlation technique comparison[J]. Friend of Science Amateurs, 2011, 3:158.
[4]
张冬,董岳,黄瑛,等.国内外污泥处理处置技术研究与应用现状[J].环境工程, 2015,(33):600. ZHANG Dong, DONG Yue, HUANG Ying,et al. Research and application situation of sludge treatment and disposal technology at home and abroad[J]. Environmental Engineering, 2015, (33):600.
[5]
翟付群,胡舒.剩余活性污泥的处置与利用[J].广西轻工业, 2009, (4):117. ZHAI Fuqun, HU Shu. Disposal and utilization of residual activated sludge[J].Guangxi Journal of Light Industry,2009, (4):117.
[6]
KARTHIK T, RATHINAMOORTHY R. Recycling and reuse of textile effluent sludge[J]. Environmental Implications of Recycling and Recycled Products, 2015, 213.
[7]
贺君,王启山,仁爱玲.污水厂污泥制轻质陶粒研究现状及应用前景[J].城市环境与城市生态,2003,16(6):13. HE Jun, WANG Qishan, REN Ailing. Use of sewage sludge for manufacturing light ceramsite[J].Urban Environment & Urban Ecology, 2003, 16(6):13.
[8]
薛红艳,战友,张劲勇,等.城市生活污水污泥理化性质分析[J].实验室研究与探索,2014, 33(9):28. XUE Hongyan, ZHAN You, ZHANG Jingyong, et al. Analysis on the physical and chemical properties of urban sewage sludge[J]. Research and Exploration in Laboratory, 2014, 33(9):28.
[9]
DJAFER A, DJAFER L, MAIMOUN B. Reuse of waste activated sludge for textile dyeing wastewater treatment by biosorption:Performance optimization and comparison[J]. Water & Environment Journal, 2017, 31(1):105.
[10]
王传虎,杨周生,葛金龙,等.石英砂尾矿尾砂综合利用研究综述[J].中国非金属矿工业导刊, 2008, (3):16. WANG Chuanhu, YANG Zhousheng, GE Jinglong, et al. Review of study on comprehensive utilization of quartz tailings and mill tailings[J]. China Non-Metallic Mining Industry Herald, 2008, (3):16.
[11]
朱健,王平,雷明倩,等.硅藻土理化性质及改性研究进展[J].中南林业科技大学学报, 2012, 32(12):61. ZHU Jian, WANG Ping, LEI Mingqian, et al. Physicochemical properties, modification and research progress of diatomite[J]. Journal of Central South University of Forestry & Technology, 2012, 32(12):61.
[12]
夏欣鹏,杨云霞,袁双龙,等.高岭土的可塑性与其矿物组成和颗粒结构的相关性能[J].耐火材料,2006,(1):75. XIA Xinpeng, YANG Yunxia, YUAN Shuanglong, et al. The plasticity of kaolin and its mineral composition and particle structure related properties[J]. RefractoryMaterials, 2006, (1):75.
[13]
许国仁,邹金龙,孙丽欣.污泥作为添加剂制备轻质陶粒的实验研究[J].哈尔滨工业大学学报,2007,39(4):557. XU Guoren, ZOU Jinglong, SUN Lixin. Utilization of dried sludge as an additive for making ceramsite[J]. Journal of Harbin Institute of Technology, 2007, 39(4):557.
[14]
ZHAI Yunbo, WEI Xianxun, ZENG Guangming, et al. Study of adsorbent derived from sewage sludge for the removal of Cd2+, Ni2+ in aqueous solutions[J]. Separation and Purification Technology, 2004, 38(2):191.
[15]
王佳福,吕剑明.利用城市污泥制备陶粒的研究[J].硅酸盐通报, 2012, 31(3):706. WANG Jiafu, LU Jianming. Research on preparation of ceramsite using city sludge[J]. Bulletin of the Chinese Ceramic Society, 2012, 31(3):706.
[16]
CHEN Howji, HSUEH Yingchih, PENG Chingfang, et al. Paper sludge reuse in lightweight aggregates manufacturing[J]. Materials, 2016, 9(11):1.
[17]
NAIR A T, AHAMMED M M. The reuse of water treatment sludge as a coagulant for post-treatment of UASB reactor treating urban wastewater[J]. Journal of Cleaner Production, 2015, 96:272.
[18]
王兴润,金宜英. 污泥烧结轻骨料调质影响研究[J].环境科学研究, 2008, 21(6):86. WANG Xingrun, JING Yiying. Research of the effect of sludge sintering lightweight aggregate[J]. Research of Environmental Sciences, 2008, 21(6):86.
[19]
郭夙堔,阮德明,邹辉煌,等.污泥和石英砂尾矿制备建材陶粒烧结时间的研究[J].材料研究与应用,2015,9(2):130. GUO Sushen, RUAN Deming, ZOU Huihuang, et al. Study of the sintering time on the effects of ceramsite made from sewage and quartz tailing[J]. Materials Research and Application, 2015, 9(2):130.
2018, Vol. 16 